Coating a thin Al/Zn layer on the surface of plastic film, will get
high self-healing Al/Zn metallized film for capacitor use.
The prominent feature of metallized film is its self healing
ability. That is, when somewhere is breakdown, short-circuit
current can make the film around the breakdown area melting and
evaporation to recover its insulation property. Thus significantly
reduce the impact on the breakdown strength by conductive defects
and weakness in paper or film, thereby improving the working field.
Generally the thickness of the metal layer is 5nm-50nm, but on the
international it can be 1nm-100nm. In terms of heat resistance,
1nm-100um is preferred, while consideration of electric properties,
5nm-50nm is more preferred.
Under the same evaporation conditions, the larger the coating
thicknessδ, the smaller square resistance (Ω/□) , the smaller the
resistance R, the greater the load current, while the worse self
Al/Zn metallized film use heavy edge evaporation method, greatly
reduce the contact resistance between the spraying area and the
cores of the film capacitors, which has improved the quality of the
Al/Zn metallized film has a better pressure resistance.
Al/Zn metallized film has a worse moisture resistance, easily
■ Types of Metallized Layer:
2. Width:Film Slit Width±0.3mm
3. Inner Diameter:75mm +1.0mm/-0.5mm
■ Roll Outer Diameter:
1. Roll films are packed in vacuum plastic bag
2. Bags are marked with lables of types
3. The bags are packed in carton cases
4. The cartons are wrapped in wooden cases or reinforced carton
1,Metallized film should be stored in its original package until its use with
temperature 5 ～35℃and humidity less than 85%RH.
2,Metallized layer is easily oxidized when exposure to moisture.
Therefore, the film should be used as soon as possible when opened.
3,The recommended temperature is 15 -25℃with humidity less than
60%RH after the package is open.
4,With original sealed package, and stored in the above mentioned
conditions, the storage time can be as following:
Al metalized Film: 12 months from the delivered date
Al/Zn Alloy metalized Film: As Zn is relatively unstable,
preservation period depends on the resistance of the film:
Less than 10 Ohms: 6 months (from delivery date)
10 Ohms to 15 Ohms: 3 months (from delivery date)
15 Ohms: 1months (from delivery date)